Growth, thermal and optical properties of a novel nonlinear optical material K3B6O10Cl

唐唐添加于 2012-2-29 22:41 | 4009 次阅读 | 0 个评论

作者
Wu H, Pan S, Yu H, Jia D, Chang A, Li H, Zhang F, Huang X
摘要
A high quality single crystal of K3B6O10Cl with dimensions up to 25 × 11 × 7 mm3 was successfully grown by the top-seeded solution growth method for the first time. Morphological analysis reveals that the growth of the crystal is anisotropic. By the minimum deviation technique, the refractive indices of the crystal were measured and fitted to the Sellmeier equations. The limit of type-I phase matching second harmonic generation wavelength was calculated to be 255 nm. The transparency spectrum shows that the as-grown crystal is transparent in the wavelength range of 180–3460 nm. The thermal properties and laser damage threshold have been investigated. The two principal coefficients of thermal expansion along a and c axis were measured to be 3.08 × 10−6 and 28.4 × 10−6 K−1.
详细资料
- 文献种类: Journal Article
- 期刊名称: CrystEngComm
- 期刊缩写: CrystEngComm
- 期卷页: 2012年第14卷第3期 799页
- ISBN: 1466-8033
学科领域自然科学 » 化学
相关链接 DOI URL

唐唐的文献笔记订阅

氯硼酸钾非线性晶体材料研究获进展

晶体照片及形貌图和折射率曲线

紫外非线性光学晶体是现代高新技术中不可或缺的关键材料，广泛应用于科学技术的各个领域。多年来对非线性光学晶体材料的研究一直是新型功能材料领域的研究热点。

中科院新疆理化技术研究所潘世烈研究员带领的光电功能材料团队，在氯硼酸钾晶体生长方面开展的科研工作取得了新进展。他们培育生长出25 × 11 × 7 mm3的高质量的单晶，并测试了其双折射率为0.04左右，预估倍频光的相匹配的最短波长为255nm，有望成为新一代的紫外倍频晶体。

相关研究成果以Growth, thermal and optical properties of a novel nonlinear optical material K3B6O10Cl为题，发表在CrystEngComm （2012, 14, 799-803）上。研究结果中的晶体被该杂志评为2月的“the Crystal Clear Image”刊出。

该研究得到国家自然科学基金、中科院知识创新工程重要方向项目、中科院“百人计划”资助。（来源：中科院新疆理化技术研究所）

管理选项： 导出文献|

评论(0 人)

求全文推荐收藏

1 人收藏

唐唐

Growth, thermal and optical properties of a novel nonlinear optical material K3B6O10Cl

作 者

摘 要

详细资料

学科领域 自然科学 » 化学

相关链接 DOI URL

唐唐 的文献笔记 订阅

评论(0 人)

1 人收藏

该用户的其他文献

作者

摘要

学科领域自然科学 » 化学

唐唐的文献笔记订阅